Thermal, dynamic-mechanical, and dielectric properties of surfactant intercalated graphite oxide filled maleated polypropylene nanocomposites

Tunghai University Institutional Repository > 理學院 > 化學系所 > 期刊論文 > Item 310901/22432

請使用永久網址來引用或連結此文件: http://140.128.103.80:8080/handle/310901/22432

題名:	Thermal, dynamic-mechanical, and dielectric properties of surfactant intercalated graphite oxide filled maleated polypropylene nanocomposites
作者:	Wang, Y., Tsai, H.-B.
貢獻者:	Department of Chemical and Materials Engineering, Tunghai University
關鍵詞:	graphite oxide;intercalation;nanocomposite;polypropylene
日期:	2012
上傳時間:	2013-05-21T09:06:17Z (UTC)
摘要:	Graphite oxide (GO) and amine surfactant intercalated graphite oxide (GOS) filled maleated polypropylene (PPgMA) nanocomposites were prepared directly by solution blending. In this study, the effects of the surfactant intercalation on the crystalline structure, thermo-mechanical, and dielectric properties of PPgMA/GO and GOS composites are reported. Wide-angle X-ray diffraction exhibited a lower intensity diffraction peak of the monoclinic (α) phase of PPgMA for PPgMA/GOS composites compared with the unfilled sample. Differential scanning calorimetry exhibited a single characteristic melting peak of monoclinic (α) crystalline phase. The incorporation of GOS hardly showed any change in Tm. However, the significant decrease in the melting enthalpy of PPgMA/GOS composite, which was lower than that of GO filled PPgMA, demonstrated the high degree of dispersion of the GOS flakes in the PPgMA matrix. Dynamical mechanical analysis indicated that incorporation of GO or GOS into PPgMA increased both the storage modulus and the glass transition temperature, due to the hydrogen bonding between GO and the maleic anhydride group of PPgMA. Dielectric analyzer showed significant increase in both dielectric permittivity and dielectric loss at high temperature regimes in the GOS nanocomposites. The finely dispersed GOS in the PPgMA matrix manifested the interfacial polarization, which gave rise to much greater ε' and ε'' than that of PPgMA/GO hybrid. ? 2011 Wiley Periodicals, Inc.
關聯:	Journal of Applied Polymer Science 123 (5) , pp. 3154-3163
顯示於類別:	[化學系所] 期刊論文